COLD FORMING MATERIALS

36 CrB4 冷镦用钢丝（CHQ）

MATERIALSENGINEERINGCREATION GROUP

产品中心 / 36 CrB4 冷镦用钢丝（CHQ）

36 CrB4 冷镦用钢丝（CHQ）

直径: 0.40-46mm

拉伸强度: 参考技术信息

Product Detail Technical Information Inspection Packaging

上海创造集团是中国专注于冷轧优质钢丝的标杆企业，整个管理团队拥有20年的行业经验。我们与多家汽车行业一级供应商建立了良好的关系，所有钢丝均来自品牌钢厂。所有订单均100%可追溯。

Specification

+AR 或 +PE

+AC 或 +AC+PE

+AR+C

+AR+C+AC

+AR+C+AC+LC

+AC+C

Specification

- : 连续且平滑

- : 无接缝、重叠、坑坑、划痕和拉拔划痕

- : 不应有锈迹

Specification

- : 汽车产业

- : 建筑业

- : 机械行业

- : 其他行业

Case Study

Products & Service

1.交货条款组合

表C.1 -交货时热处理条件、产品形式和适用要求的组合

Heat-treatment condition at delivery

Symbo

Products form a

Applicable requirements in cases where the steel concerned has been ordered with reference to the steel names indicated in

Wire rod

Bar

Wire

Tables C.2,C.3,C.4, C.5 or C.6

Tables C.2,C.3,C.4,C.5,C,6,C.Z C.8 or C.9

Tables C.2,C.3,C.4,C.5,C.6 or C.10

Optional

As hot-rolled or peeled

+AR or +PE

Chemical compo- sition as speci- fied in Tables C.2 and C.3

Me- chanical properties as spec- ified in Tables C.4. C.5 and C.6

Chemical compo- sition as speci- fied in Tables C.2 and C.3

Me- chanical properties as spec- ified in Tables C.4, C.5 and C.6

Values for harden- ability according to Tables C.Z C.8 and C.9

Chemical compo- sition as speci- fied in Tables C.2 and C.3

Me- chanical properties as spec- ified in Tables C.4. C.5 and C.6

Mini- mum core hardness and max- imum diameter accord- ing to TableC.10

Supplementa- ry or special requirements as specified in Annex Eb

Cold drawn

+AR +C

—

Cold drawn + spheroidized

+AR+C+ AC

—

Cold drawn + spheroidized + skin passed

+AR+C +AC +LC

—

Spheroidized or spheroidized + peeled

+AC or +AC+PE

Spheroidized + cold drawn

+AC+C

—

Spheroidized+ cold drawn +spheroidized

+AC+C+ AC

Spheroidized + cold drawn +sphe- roidized +skin passed

+AC+C+ AC+LC

Others

Other delivery conditions may be agreed at the time of ordering

a X=applicable,—=not applicable b If agreed at the time of the enquiry and order.

2.化学成分

表C.3-调质用含氮合金钢牌号的化学成分（适用于铸造分析）

Steel name b

% mass fraction

Si c

Cr d

17B2

0,15 to 0,20

0,30

0,60 to 0,90

0,025

0,30

0,0008 to 0,005

0,25

23B2

0,20 to 0,25

0,30

0,60 to 0,90

0,025

0,30

0,0008 to 0,005

0,25

28B2

0,25 to 0,30

0,30

0,60 to 0,90

0,025

0,30

——

0,0008 to 0,005

0,25

33B2

0,30 to 0,35

0,30

0,60 to 0,90

0,025

0,30

—

0,0008 to 0,005

0,25

38B2

0,35 to 0,40

0,30

0,60 to 0,90

0,025

0,30

—

0,0008 to 0,005

0,25

23MnB3

0,21 to 0,25

0,15

0,80 to 1,00

0,015

0,25 to 0,35

—

0,0008 to 0,005

0,25

17MnB4

0,15 to 0,20

0,30

0,90 to 1,20

0,025

0,30

—

0,0008 to 0,005

0,25

20MnB4

0,18 to 0,23

0,30

0,90 to 1,20

0,025

0,30

0,0008 to 0,005

0,25

23MnB4

0,20 to 0,25

0,30

0,90 to 1,20

0.025

0,025

0,30

—

0,0008 to 0,005

0,25

27MnB4

0,25 to 0,30

0,30

0,90 to 1,20

0,025

0,30

—

0,0008 to 0,005

0,25

30MnB4

0,27 to 0,32

0,30

0,80 to 1,10

0,025

0,30

—

0,0008 to 0,005

0,25

36MnB4

0,33 to 0,38

0,30

0,80 to 1,10

0,025

0,30

—

0,0008 to 0,005

0,25

20MnB5

0,17 to 0,23

0,30

1,10 to 1,40

0,025

0,30

—

0,0008 to 0,005

0,25

23MnB5

0,20 to 0,26

0,30

1,10 to 1,40

0,025

0,30

—

0,0008 to 0,005

0,25

26MnB5

0,23 to 0,29

0,30

1,20 to 1,50

0,025

0,30

—

0,0008 to 0,005

0,25

34MnB5

0,31 to 0,37

0,30

1,20 to 1,50

0,025

0,30

—

0,0008 to 0,005

0,25

37MnB5

0,35 to 0,40

0,30

1,15 to 1,45

0,025

0,30

—

0,0008 to 0,005

0,25

30MoB1

0,28 to 0,32

0,30

0,80 to 1,00

0,025

0,30e

0,08 to 0,12

0,0008 to 0,005

0,25

provided that they do not exceed 0,01 %for carbon and the values indicated in Table 2 for the other elements.

Elements not quoted in this table should not be intentionally added to the steel without the agreement of the purchaser,except those intended for finishing the heat.All reasonable precautions shall be taken in order to prevent the addition of such elements from scrap or other materials used in the production process,which can affect the hardenability, mechanical properties and applicability To improve the performance of cold heading,it is possible to add Al:0,020 %to 0,050 %.

a b

Maximum values unless otherwise indicated. In the case of steels with hardenability requirements (see Table C.8),minor deviations from the specified limits are permitted (with the exception of sulfur and phosphorus) c Lower silicon contents may be agreed at the time of ordering,in which case due consideration should be given to the effects that could result for what concerns the specified properties such as,for example,hardenability. d Where a maximum chromium content of 0,30 %is specified,a minimum level may also be agreed at the time of enquiry and order e In order to obtain a core hardening for the steel grade 30MoB1,the lower limit of Cr shall be 0,15 %and may be agreed at the time of enquiry and order.For certain applications, the higher limit for Cr may also be lowered by agreement at time of enquiry and order.

3.力学性能

表C.6 -含氮合金钢牌号的机械性能

Steel name	Diameter		Delivery condition
			+AR or +PE		+AC or +AC+PE		+AR+C		+AR+C+AC		+AR+C+AC+LC		+AC+C
			Mechanical properties
	above mm	up to mm	Rm max. MPa	Z min. %	Rm max. MPa	Z min. %	Rm max MPa	Z min. %	Rm max. MPa	Z min. %	Rm max. MPa	Z min. %	Rm max. MPa	Z min. %
20MnB4	2	5				—			490	68	530	66		—
	5	10	580	60	500	66	680	55	480	68	520	66	600	61
	10	25	580	60	500	66	670	55	480	68	520	66	590	61
23MnB4	2	5							510	66	550	64	—
	5	10	600	60	520	64	700	55	500	66	540	64	620	59
	10	25	600	60	520	64	690	55	500	66	540	64	610	59
27MnB4	2	5					—	—	530	65	570	63
27MnB4	5	40	—		540	63		—	520	65	560	63	640	58
30MnB4	2	5	一	—			—		560	65	600	63	—	—
30MnB4	5	40	——	—	570	63		—	550	65	590	63	670	58
36MnB4	2	5	—	——	一		—	——	590	64	630	62		—
36MnB4	5	40	—	—	600	62	—	—	580	64	620	62	700	57
20MnB5	2	5						—			630	55	—
20MnB5	5	40		—		一	—	—	—		630	55	630	55
23MnB5	2	5	—	—	—	—	—	—	—	—	640	55		—
23MnB5	5	40	—		—	—		—	—	—	640	55	640	55
26MnB5	2	5	—		一	—		—		一	650	55	—	—
26MnB5	5	40	—			—	—	—			650	55	650	55
34MnB5	2	5	—	—	—	—	—		—	—	680	55	—	—
34MnB5	5	40	—	—	一		一	—		一	680	55	680	55
37MnB5	2	5						—	610	64	650	62		—
37MnB5	5	40	—		620	62	—	—	600	64	640	62	720	57
It should be recognized in the +AR condition that the tensile strength values are not compatible with the whole range of composition given in TableC.3 for a steel grade.Care should be taken that,depending on diameter and composition supplied,the tensile strength values are compatible with the hardenability requirements.